Products:VYLOPET



TOYOBO ECOVYLOPET®

PET bottle recycling grades

Features

  1. Having made significant improvement in appearances, fluidity and mold release easiness, ECOVYLOPET® can be processed much easier than general PET for injection molding.
  2. It is adaptable for large auto-parts and industrial product parts.
  3. With a specific miscibility method, its impact resistance has greatly been enhanced.



    Comparisons of ECOVYLOPET® with polyamide resins

 

Application examples

Engine head covers of automobiles
Hot plates
Engine head covers of automobile
Vending machine parts
Umbrella ribs

Lists of VYLOPET Basic Properties
Property itemsUnitGF 10% reinforced typeGF 30% reinforced type
EMC2310
(General purpose type)
EMC2311
(General purpose type)
EMC2330
(General purpose type)
Specific weight1.591.381.59
Water absorption
23°C×24h
%0.060.050.06
Molding shrinkage
Flow direction(2 mmt)
Perpendicular direction
%
%
0.4
0.9
0.4
0.9
0.3
0.9
Tensile strength
Tensile elasticity
MPa
%
100
2.2
80
3.1
142
2.2
Flexural strength
Young’s modulus
Flexibility modulu
MPa
GPa
%
142
7.1
2.6
125
4.2
4.3
195
10.0
2.7
IZOD Notch toughness impact testJ / m64.070.081.0
Rockwell’s hardnessM-scale909095
Thermal deformation 455 KPa
Temperature1820 KPa
°C
°C
235
210
235
205
245
220
Coefficient of linear thermal expansion×10-5cm / cm / °C4.04.04.0
Optimum mold temperature°C110120110

 

Property itemsUnitFiller 15% reinforced type
EMC2301
(General purpose type)
EMC2301E
(Modified type)
Specific weight1.441.35
Water absorption
23°C×24h
%0.060.05
Molding shrinkage

Flow direction(2 mmt)
Perpendicular direction
%
%
1.2
1.3
1.2
1.2
Tensile strength
Tensile elasticity
MPa
%
55
1.8
65
3.0
Flexural strength
Young’s modulus
Flexibility modulus
MPa
GPa
%
100
4.4
2.6
105
3.8
3.7
IZOD Notch toughness impact testJ / m40.045.0
Rockwell’s hardnessM-scale9090
Thermal deformation 455 KPa
Temperature1820 KPa
°C
°C
200
205
Coefficient of linear thermal expansion
×10-5
cm / cm / °C4.54.5
Optimum mold temperature°C110120